316/316L/316Ti സ്റ്റെയിൻലെസ്സ് സ്റ്റീൽ കോയിൽ
വിവരണം
| ടൈപ്പ് ചെയ്യുക | ഗ്രേഡ് | ഗ്രേഡ് | രാസഘടകം % | ||||||||||
| C | Cr | Ni | Mn | P | S | Mo | Si | Cu | N | മറ്റുള്ളവ | |||
| ഓസ്റ്റെനിറ്റിക് | 201 | SUS201 | ≤0.15 | 16.00-18.00 | 3.50-5.50 | 5.50-7.50 | ≤0.060 | ≤0.030 | - | ≤1.00 | - | ≤0.25 | - |
| 202 | SUS202 | ≤0.15 | 17.00-19.00 | 4.00-6.00 | 7.50-10.00 | ≤0.060 | ≤0.030 | ≤1.00 | - | ≤0.25 | - | ||
| 301 | 1.431 | ≤0.15 | 16.00-18.00 | 6.00-8.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | ≤0.10 | - | |
| 304 | 1.4301 | ≤0.07 | 17.00-19.00 | 8.00-10.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | - | |
| 304L | 1.4307 | ≤0.030 | 18.00-20.00 | 8.00-10.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | - | |
| 304H | 1.4948 | 0.04-0.10 | 18.00-20.00 | 8.00-10.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | - | |
| 309 | 1.4828 | ≤0.20 | 22.00-24.00 | 12.00-15.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | - | |
| 309 എസ് | * | ≤0.08 | 22.00-24.00 | 12.00-15.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | - | |
| 310 | 1.4842 | ≤0.25 | 24.00-26.00 | 19.00-22.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.50 | - | - | - | |
| 310S | * | ≤0.08 | 24.00-26.00 | 19.00-22.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.50 | - | - | - | |
| 314 | 1.4841 | ≤0.25 | 23.00-26.00 | 19.00-22.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | 1.50-3.00 | - | - | - | |
| 316 | 1.4401 | ≤0.08 | 16.00-18.50 | 10.00-14.00 | ≤2.00 | ≤0.045 | ≤0.030 | 2.00-3.00 | ≤1.00 | - | - | - | |
| 316L | 1.4404 | ≤0.030 | 16.00-18.00 | 10.00-14.00 | ≤2.00 | ≤0.045 | ≤0.030 | 2.00-3.00 | ≤1.00 | - | - | - | |
| 316Ti | 1.4571 | ≤0.08 | 16.00-18.00 | 10.00-14.00 | ≤2.00 | ≤0.045 | ≤0.030 | 2.00-3.00 | ≤1.00 | - | 0.1 | Ti5(C+N)~0.70 | |
| 317 | * | ≤0.08 | 18.00-20.00 | 11.00-15.00 | ≤2.00 | ≤0.045 | ≤0.030 | 3.00-4.00 | ≤1.00 | - | 0.1 | - | |
| 317L | 1.4438 | ≤0.03 | 18.00-20.00 | 11.00-15.00 | ≤2.00 | ≤0.045 | ≤0.030 | 3.00-4.00 | ≤1.00 | - | 0.1 | - | |
| 321 | 1.4541 | ≤0.08 | 17.00-19.00 | 9.00-12.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | Ti5(C+N)~0.70 | |
| 321H | * | 0.04-0.10 | 17.00-19.00 | 9.00-12.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | Ti5(C+N)~0.70 | |
| 347 | 1.455 | ≤0.08 | 17.00-19.00 | 9.00-12.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | Nb≥10*C%-1.10 | |
| 347H | 1.494 | 0.04-0.10 | 17.00-19.00 | 9.00-12.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | Nb≥10*C%-1.10 | |
| xm-19 | നൈട്രോണിക്50 | ≤0.06 | 20.50-23.50 | 11.50-13.50 | 4.0-6.0 | ≤0.045 | ≤0.030 | 1.50-3.00 | ≤1.00 | - | 0.2-0.4 | Nb:0.10-0.30 V:0.10-0.30 | |
| 904L | N08904 | ≤0.02 | 19.0-23.0 | 23.0-28.0 | 4.0-5.0 | ≤0.045 | ≤0.035 | ≤1.00 | 0.1 | ക്യൂ:1.0-2.0 | |||
| ഡ്യൂപ്ലക്സ് | 2205 | എസ് 32205 | ≤0.03 | 22.0-23.0 | 4.5-6.5 | ≤2.00 | ≤0.030 | ≤0.020 | 3.0-3.5 | ≤1.00 | - | 0.14-0.20 | |
| 2507 | എസ് 32750 | ≤0.03 | 24.0-26.0 | 6.0-8.0 | ≤1.20 | ≤0.035 | ≤0.020 | 3.0-5.0 | ≤0.80 | 0.5 | 0.24-0.32 | ||
| * | എസ് 32760 | ≤0.03 | 24.0-26.0 | 6.0-8.0 | ≤1.00 | ≤0.030 | ≤0.010 | 3.0-4.0 | ≤1.00 | 0.5-1.00 | 0.2-0.3 | ||
| 2304 | എസ് 32304 | ≤0.03 | 21.5-24.5 | 3.0-5.5 | ≤2.50 | ≤0.040 | ≤0.030 | 0.05-0.6 | ≤1.00 | 0.05-0.6 | 0.05-0.2 | ||
| 329 | 1.446 | ≤0.08 | 23.00-28.00 | 2.00-5.00 | ≤1.00 | ≤0.040 | ≤0.030 | 1.00-2.00 | ≤0.75 | - | - | ||
| ഫെറൈറ്റ് | 409 | എസ് 40900 | ≤0.03 | 10.50-11.70 | 0.5 | ≤1.00 | ≤0.040 | ≤0.020 | - | ≤1.00 | - | ≤0.030 | Ti6(C+N)~0.50 Nb:0.17 |
| 430 | 1Cr17 | ≤0.12 | 16.00-18.00 | - | ≤1.0 | ≤0.040 | ≤0.030 | - | ≤1.0 | - | - | - | |
| 444 | എസ് 44400 | ≤0.025 | 17.50-19.50 | 1 | ≤1.00 | ≤0.040 | ≤0.030 | 1.75-2.5 | ≤1.00 | - | 0.035 | Ti+Nb:0.2+4(C+N)~0.80 | |
| 446 | എസ് 44600 | ≤0.20 | 23.00-27.00 | 0.75 | ≤1.5 | ≤0.040 | ≤0.030 | 1.50-2.50 | ≤1.00 | - | ≤0.25 | - | |
| മാർട്ടൻസൈറ്റ് | 410 | 1Cr13 | 0.08-0.15 | 11.50-13.50 | 0.75 | ≤1.00 | ≤0.040 | ≤0.030 | - | ≤1.00 | - | - | - |
| 410S | * | ≤0.080 | 11.50-13.50 | 0.6 | ≤1.00 | ≤0.040 | ≤0.030 | - | ≤1.00 | - | - | - | |
| 416 | Y1Cr13 | ≤0.15 | 12.00-14.00 | 3) | ≤1.25 | ≤0.060 | ≥0.15 | - | ≤1.00 | - | - | - | |
| 420 | 2Cr13 | ≥0.15 | 12.00-14.00 | - | ≤1.00 | ≤0.040 | ≤0.030 | - | ≤1.00 | - | - | - | |
| 420J2 | 3Cr13 | 0.26-0.35 | 12.00-14.00 | - | ≤1.00 | ≤0.040 | ≤0.030 | - | ≤1.00 | - | - | - | |
| 431 | 1Cr17Ni2 | ≤0.20 | 15.00-17.00 | 1.50-2.50 | ≤1.00 | ≤0.040 | ≤0.030 | - | ≤0.80 | - | - | - | |
| 440C | 11Cr17 | 0.95-1.20 | 16.00-18.00 | - | ≤1.00 | ≤0.040 | ≤0.030 | 0.75 | ≤1.00 | - | - | - | |
| PH | 630 | 17-4PH | ≤0.07 | 15.00-17.50 | 3.00-5.00 | ≤1.00 | ≤0.035 | ≤0.030 | - | ≤1.00 | 3.00-5.00 | - | Nb 0.15-0.45 |
| 631 | 17-7PH | ≤0.09 | 16.00-18.00 | 6.50-7.50 | ≤1.00 | ≤0.035 | ≤0.030 | - | ≤1.00 | ≤0.50 | - | അൽ 0.75-1.50 | |
| 632 | 15-5PH | ≤0.09 | 14.00-16.00 | 3.50-5.50 | ≤1.00 | ≤0.040 | ≤0.030 | 2.00-3.00 | ≤1.00 | 2.5-4.5 | - | അൽ 0.75-1.50 | |
സ്റ്റെയിൻലെസ്സ് സ്റ്റീൽ ഷീറ്റ് പ്ലേറ്റ് ഗ്രേഡ് ബാഗു വിതരണം
| ഉപരിതല ഫിനിഷ് | സവിശേഷതകളും പ്രയോഗവും |
| 2B | no 2B യുടെ ഉപരിതല തെളിച്ചവും പരന്നതയും no2D നേക്കാൾ മികച്ചതാണ്.പിന്നീട് അതിന്റെ മെക്കാനിക്കൽ ഗുണങ്ങൾ മെച്ചപ്പെടുത്തുന്നതിനുള്ള ഒരു പ്രത്യേക ഉപരിതല ചികിത്സയിലൂടെ, No2B ന് സമഗ്രമായ ഉപയോഗങ്ങൾ ഏതാണ്ട് തൃപ്തിപ്പെടുത്താൻ കഴിയും. |
| നമ്പർ 1 | ഗ്രിറ്റ്#100-#200 എന്ന ഉരകൽ ബെൽറ്റ് ഉപയോഗിച്ച് പോളിഷ് ചെയ്ത, തുടർച്ചയായ പരുക്കൻ സ്‌ട്രിയയ്‌ക്കൊപ്പം മികച്ച തെളിച്ചമുണ്ട്, കെട്ടിടം, ഇലക്ട്രിക്കൽ വീട്ടുപകരണങ്ങൾ, അടുക്കള പാത്രങ്ങൾ തുടങ്ങിയവയ്‌ക്ക് ആന്തരികവും ബാഹ്യവുമായ ആഭരണങ്ങളായി ഉപയോഗിക്കുന്നു. |
| നമ്പർ 4 | ഗ്രിറ്റ് #150-#180 എന്ന ഉരകൽ ബെൽറ്റ് ഉപയോഗിച്ച് മിനുക്കി, തുടർച്ചയായ പരുക്കൻ സ്‌ട്രിയയ്‌ക്കൊപ്പം മികച്ച തെളിച്ചമുണ്ട്, പക്ഷേ No3 നേക്കാൾ കനംകുറഞ്ഞത്, ബാത്ത്‌ടബ് കെട്ടിടങ്ങൾക്ക് ആന്തരികവും ബാഹ്യവുമായ ആഭരണങ്ങളായി ഉപയോഗിക്കുന്നു ഇലക്ട്രിക്കൽ വീട്ടുപകരണങ്ങൾ അടുക്കള പാത്രങ്ങൾ, ഭക്ഷ്യ സംസ്‌കരണ ഉപകരണങ്ങൾ മുതലായവ. |
| HL | NO.4 ഫിനിഷിൽ ഗ്രിറ്റ് #150-#320 എന്ന ഉരച്ചിലുകളുള്ള ബെൽറ്റ് ഉപയോഗിച്ച് മിനുക്കിയതും തുടർച്ചയായ വരകളുള്ളതുമാണ്, പ്രധാനമായും കെട്ടിടങ്ങളുടെ ആഭരണങ്ങളായ എലിവേറ്ററുകൾ, കെട്ടിടത്തിന്റെ വാതിൽ, മുൻഭാഗത്തെ പ്ലേറ്റ് മുതലായവ. |
| BA | കോൾഡ് റോൾഡ്, ബ്രൈറ്റ് അനീൽഡ്, സ്കിൻ-പാസ്ഡ്, ഉൽപ്പന്നത്തിന് മികച്ച തെളിച്ചവും കണ്ണാടി, അടുക്കള ഉപകരണം, ആഭരണം മുതലായവ പോലെ നല്ല പ്രതിഫലനവുമുണ്ട്. |
| 8K | ഉൽപ്പന്നത്തിന് മികച്ച തെളിച്ചമുണ്ട്, കണ്ണാടിയാകാൻ റിഫ്ലെക്സിവിറ്റിക്ക് മുൻഗണന നൽകുന്നു. |